In Vitro Microleakage and Fracture Resistance of "Infinity Edge" and Cusp Reduction Preparation Designs for Moderate-sized Class II Composites.

AIM: This study aimed to evaluate the marginal microleakage and maximum occlusal fracture loads and fracture modes of two novel class II preparation designs, "infinity edge" and the "2.5 mm cusp reduction" preparations as compared to a traditional class II preparation without cuspal involvement. MATERIALS AND METHODS: Thirty extracted human mandibular molars were prepared for moderate-sized class II restorations with extensions into all occlusal grooves. Of these, ten class II preparations served as control. Ten were modified for a 2.5 mm even reduction of the cusps adjacent to the interproximal box. An additional 10 preparations were modified with an "infinity edge" bevel on the interproximal and occlusal portions. All teeth were restored utilizing a flowable bulk-fill composite in the apical portion of the interproximal box and 2-4 mm of heated bulk-fill composite in one increment for the remainder. All groups were cyclic loaded and thermocycled, then imaged with microcomputed tomography (µCT) before and after infiltration with a silver nitrate solution. Images were subtracted to obtain volumetric measurements of microleakage and reported as a percentage of the total volume from the apical extent of the proximal box. All groups were loaded to failure and fracture load and mode were recorded. RESULTS: No significant differences were found in microleakage volume as a percentage of total tooth volume; however, the "infinity edge" group had significantly greater microleakage in the proximal box compared to the traditional class II group. No significant differences were found in fracture load or mode between the groups. CONCLUSION: Traditional class II, 2.5 mm cuspal reduction, and "infinity edge" preparation designs have similar fracture loads as well as volumes of microleakage; however, an "infinity edge" preparation has a higher ratio of microleakage in the proximal box. CLINICAL SIGNIFICANCE: Clinicians should carefully consider the use of "infinity edge" margins, particularly on dentin in the apical extent of the proximal box. How to cite this article: Watson JC, Lien W, Raimondi JC, et al. In Vitro Microleakage and Fracture Resistance of "Infinity Edge" and Cusp Reduction Preparation Designs for Moderate-sized Class II Composites. J Contemp Dent Pract 2024;25(1):3-9.

Novel chairside spectrometer-trained system for measuring the irradiance of light-curing units.

The purpose of this study was to compare the performances of 5 different instruments in measuring the irradiance of light-curing units (LCUs). A novel spectrometer-trained radiometer (CheckUp), 2 conventional chairside radiometers (Bluephase Meter I and Bluephase Meter II), and 2 devices considered to be gold standards for measuring irradiance (an integrating sphere spectrometer and a thermopile sensor) were used to evaluate 7 LCUs. The irradiance of each LCU was measured 10 times with each meter. Data were analyzed using linear regression analysis and a 1-way analysis of variance with Tukey post hoc test (α = 0.05). The mean irradiance values of the LCUs differed significantly depending on which meter was used for measurement (P < 0.05). Bivariate regression analysis demonstrated that the highest correlations in the irradiance values were found between the CheckUp meter and both the integrating sphere (r2 = 0.980) and the thermopile (r2 = 0.933). The absolute mean (SD) percentage deviation between irradiance measured by the CheckUp instrument and irradiance measured by the other meters was 7.2% (2.0%) for the integrating sphere, 7.0% (3.6%) for the thermopile, 21.5% (16.1%) for Bluephase Meter I, and 13.1% (7.1%) for Bluephase Meter II. Compared with the 2 conventional chairside radiometers, the CheckUp meter provided the highest correlation with and lowest absolute percentage deviation from the irradiance measured by the gold standard spectrometers.

Bond strength of resin cements to dentin using universal bonding agents.

PURPOSE: To determine the effect of new universal bonding agents on the bond strength of dual-cure resin cements to dentin. METHODS: 140 extracted human third molars were mounted in dental stone and sectioned with a saw to remove coronal tooth structure. The teeth were randomly divided into seven groups of 20, based on the use of five universal bonding agents (All-Bond Universal; FuturaBond U; Prime&Bond Elect; Scotchbond Universal; Clearfil Universal) compared to two self-etch bonding agents (Clearfil SE Bond and Clearfil SE Bond 2). Each group was further divided into two equal subgroups of 10 specimens each with each subgroup tested with either self- or light-cure activation of the dual-cure resin cement (Calibra). The bonding agent was applied per manufacturers' instructions to the dentin surface of each specimen. The specimens were placed into a jig and resin cement was inserted into the mold to a height of 3-4 mm and light cured. Specimens were stored for 24 hours in 37 degrees C distilled water and tested in shear in a universal testing machine. A mean shear bond strength value (MPa) and standard deviation was determined per group. RESULTS: Except for Clearfil Universal, the new simplified universal bonding agents resulted in significantly lower shear bond strength of the resin cement to dentin than the two-step, self-etching bonding agents Clearfil SE Bond or Clearfil SE Bond 2.